ProTXcoat 301CRSG

High Build Solvent Free Epoxy

High Build Solvent Free Chemical Resistant Coating

301CRSG is a high performance solvent free coating designed for aggressive environments.

301CRSG is based on a special liquid epoxy polymer reacted with a blend of amine and polyamino resins reinforced with inert pigments and silicas which produces a system with exceptional mechanical, chemical and corrosion resistance.

301CRSG offers excellent adhesion to steel and concrete and has outstanding abrasion and erosion resistance making it ideal for tanks, containment areas, steelwork and floors.

Before proceeding, please read the following information carefully to ensure that the correct application procedure is fully understood.

TECHNICAL SPECIFICATIONS

Steel Surfaces – Surfaces should then be abrasive blast cleaned to a minimum Sa21⁄2 – Sa3 BS7079 Part A1 : 1989 or equivalent with a blast profile of 75 – 125 microns corresponding to ‘Rough’ in ISO 8503/1. All loose abrasive dust and debris must be blown clear or vacuum cleaned away.

Steel surfaces do not require priming but should be coated within 4 hours of blast cleaning to prevent rash rusting.

Concrete Surfaces – All concrete to be coated should either be lightly abrasive blast cleaned using wet or dry abrasive techniques or alternatively high pressure water jetting. Care must be taken not to expose the aggregate in the concrete. All dust and abrasive material shall be removed from the surface prior to coating.

312CRX is a two component material comprising base and activator components which must be mixed together prior to use.

Stir the contents of the base component, continue stirring and gradually add the total contents of the activator container, stir the combined mix until completely homogenous.

The mixed materials should be used within 25-30 minutes of mixing at 20°C (68°F). This time will be reduced at higher temperatures and extended at lower temperatures.

Application should not be carried out at temperatures below 5°C nor when relative humidity exceeds 85% or when the surface to be coated is less than 3°C above the dew point.

301CRSG is suitable for application by brush or roller, using good quality brushes or short to medium pile rollers.

On concrete surfaces it is important to stipple the 301 into the primed surface to ensure good wetting of the surface. Technology at work for you

Coverage Rate
2.24sqm per kg at 250 microns
3.4L equals 13.6 m/2 1t 250 microns

Detailed working recommendations are available from the Technical Centre on request.

Mixing RatioBaseActivator
2.41 By volume
41 By weight
AppearanceBaseDark Grey liquid
ActivatorAmber fluid
Drying & Cure Times at 20°C(68°F)UsableLife25minutes
Initial Set6 hours
Min Overcoat6 hours
Max Overcoat36 hours
Volume Solids100%
V.O.C.Nil
Shelf LifeUse within 5 years of purchase. Store in original sealed containers at temperatures between 5°C (40°F) and 30°C (86°F).

Abrasion Resistance 60 mgm loss per1000 cycles ASTM D 4060 1 kg load – CS17 wheel

Impact Resistance 2.6 joules ASTMG14

Dry Heat Resistance 100oC (212oF) ASTMD2485

Water Vapour Permeability 3.75×10-6perm.cm ASTM D1653

Salt Fog Resistance Excellent, unaffected after ASTMB117 10,000 hrs exposure

Humidity Resistance Unaffected 5,000hrs BS 3900 Part F2

Direct Pull Adhesion 98 kg/cm2(1400 psi) Steel ASTMD4541

As long as normal good practice is observed 301CRSG can be safely used.

Protective gloves should be worn during use.

A fully detailed Safety Data Sheet is either included with the material or is available on request.

Supplied in 5kg and 20kg packs

TheinformationprovidedinthisProductDataSheetisintendedasageneral guide only and should not be used for specification purposes. The information is given in good faith but we assume no responsibility for the use made of the productorthis information because this is outside the control of the company. Users should determine the suitability of the product for their own particular purposes by their own tests.